ISO 1099:2026
2026-10
Вы можете ознакомиться с данным стандартом в нашей онлайн-библиотеке (OBP)
ISO 1099:2026
Тезис
This document specifies the conditions for conducting axial, constant-amplitude, force-controlled, fatigue tests at ambient, elevated, and low temperature on metallic specimens, without deliberately introduced stress concentrations. The object of testing while employing this document is to provide fatigue information, such as the relation between applied stress and number of cycles to failure for a given material condition, such as microstructure, at various stress ratios.
While the form, preparation and testing of specimens of circular and rectangular cross-section are described, component testing and other specialized forms of testing are not included in this document.
NOTE 1 Fatigue tests on notched specimens are not covered by this document since the shape and size of notched test pieces have not been standardized. However, fatigue-test procedures described in this document can be applied to fatigue tests of such notched specimens.
NOTE 2 Throughout this document, the engineering stress is employed. Engineering stress is equal to the axially applied force divided by the cross-sectional area of the test specimen, S = Force/Area, [MPa], at the test temperature.
Общая информация
-
Текущий статус: ОпубликованоДата публикации: 2026-10Этап: Опубликование международного стандарта [60.60]
-
Версия: 4
-
Технический комитет :ISO/TC 164/SC 4ICS :77.040.10
- RSS обновления
Жизненный цикл
-
Ранее
ОтозваноISO 1099:2017
-
Сейчас
-
00
Предварительная стадия
-
10
Стадия, связанная с внесением предложения
-
20
Подготовительная стадия
-
30
Стадия, связанная с подготовкой проекта комитета
-
40
Стадия, связанная с рассмотрением проекта международного стандарта
-
50
Стадия, на которой осуществляется принятие стандарта
-
60
Стадия, на которой осуществляется публикация
-
90
Стадия пересмотра
-
95
Стадия, на которой осуществляется отмена стандарта
-
00