This document specifies a method of converting room temperature percentage elongations after fracture obtained on various proportional and non-proportional gauge lengths to other gauge lengths.

Formula (1), on which conversions are based, is considered to be reliable when applied to carbon, carbon manganese, molybdenum and chromium molybdenum steels within the tensile strength range 300 N/mm2 to 700 N/mm2 and in the hot-rolled, hot-rolled and normalized or annealed conditions, with or without tempering.

These conversions are not applicable to:

a) cold reduced steels;

b) quenched and tempered steels;

c) austenitic steels.

These conversions are not applicable when the gauge length exceeds  or where the width to thickness ratio of the test piece exceeds 20.


Общая информация

  • Текущий статус :  Published
    Дата публикации : 2021-12
  • Версия : 3
  • :
    ISO/TC 17/SC 20
    General technical delivery conditions, sampling and mechanical testing methods
  • 77.040.10
    Mechanical testing of metals

Цели в области устойчивого развития

Данный стандарт разработан для достижения следующих Цель устойчивого развития:

Приобрести данный стандарт

Формат Язык
PDF + ePub
Бумажный
  • CHF138

Жизненный цикл


Появились вопросы?

Ознакомьтесь с FAQ

Работа с клиентами
+41 22 749 08 88

Часы работы:
Понедельник – пятница: 09:00-12:00, 14:00-17:00 (UTC+1)

Будьте в курсе актуальных новостей ИСО

Подписывайтесь на наши новости, обзоры, а также на информацию о продуктах.