This document describes procedures for measuring average grain size derived from a two-dimensional polished cross-section using electron backscatter diffraction (EBSD). This requires the measurement of orientation, misorientation and pattern quality factor as a function of position in the crystalline specimen[1]. The measurements in this document are made on two dimensional sections. The reader should note carefully the definitions used (3.3) which draw a distinction between the measured sectional grain sizes, and the mean grain size which can be derived from them that relates to the three dimensional grain size.

NOTE 1 While conventional methods for grain size determination using optical microscopy are well-established, EBSD methods offer a number of advantages over these techniques, including increased spatial resolution and quantitative description of the orientation of the grains.

NOTE 2 The method also lends itself to the measurement of the grain size of complex materials, for example those with a significant duplex content.

NOTE 3 The reader is warned to interpret the results with care when attempting to investigate specimens with high levels of deformation.


Общая информация

  • Текущий статус :  Published
    Дата публикации : 2020-07
  • Версия : 2
  • :
    ISO/TC 202
    Microbeam analysis
  • 71.040.50
    Physicochemical methods of analysis

Приобрести данный стандарт

Формат Язык
PDF + ePub
Бумажный
  • CHF118

Жизненный цикл


Появились вопросы?

Ознакомьтесь с FAQ

Работа с клиентами
+41 22 749 08 88

Часы работы:
Понедельник – пятница: 09:00-12:00, 14:00-17:00 (UTC+1)

Будьте в курсе актуальных новостей ИСО

Подписывайтесь на наши новости, обзоры, а также на информацию о продуктах.