This document describes an ultrasonic wave propagation method for determining the storage components of the longitudinal complex modulus L* and the shear complex modulus G* of polymers at discrete frequencies typically in the range 0,5 MHz to 5 MHz. The method is suitable for measuring materials with storage moduli in the range 0,01 GPa to 200 GPa and with loss factors below 0,1 at around 1 MHz. With materials that have a higher loss, significant errors in velocity measurement are introduced through waveform distortion and can only be reduced using procedures that are outside the scope of this document.

The method allows measurements to be made on small specimens, typically 50 mm × 20 mm × 5 mm, or small regions of larger specimens or sheets. It is therefore possible to obtain information on the homogeneity or anisotropy (see 10.5) of modulus in a specimen.


Informations générales

  • État actuel :  Publiée
    Date de publication : 2019-04
  • Edition : 2
  • :
    ISO/TC 61/SC 5
    Propriétés physicochimiques
  • 83.080.01
    Plastiques en général

Acheter cette norme

Format Langue
PDF + ePub
Papier
  • CHF58

Vous avez une question?

Consulter notre FAQ

Service à la clientèle
+41 22 749 08 88

Horaires d’ouverture:
De lundi à vendredi - 09:00-12:00, 14:00-17:00 (UTC+1)

Suivez l'actualité de l'ISO

Inscrivez-vous à notre Newsletter (en anglais) pour suivre nos actualités, points de vue et informations sur nos produits.